Resin Type: |
Acrylic Emulsion |
Appearance: |
Milky White Liquid (becomes Transparent/elastic Film After Drying) |
Density: |
1.02 – 1.30 G/cm³ |
PH Value: |
6.5 – 9.0 |
Water Absorption Of Film: |
≤8% (24h Immersion) |
Freeze-Thaw Stability: |
5 Cycles, No Coagulation |
VOC Content: |
≤50 (Environmentally Friendly) |
Adhesion Strength: |
0.5 – 1.3 MPa |
Tensile Strength: |
≥1.0 – 1.8 MPa |
Film Breathability: |
Good Water Vapor Permeability |
Resin Type: |
Acrylic Emulsion |
Appearance: |
Milky White Liquid (becomes Transparent/elastic Film After Drying) |
Density: |
1.02 – 1.30 G/cm³ |
PH Value: |
6.5 – 9.0 |
Water Absorption Of Film: |
≤8% (24h Immersion) |
Freeze-Thaw Stability: |
5 Cycles, No Coagulation |
VOC Content: |
≤50 (Environmentally Friendly) |
Adhesion Strength: |
0.5 – 1.3 MPa |
Tensile Strength: |
≥1.0 – 1.8 MPa |
Film Breathability: |
Good Water Vapor Permeability |
Acrylic Emulsion Waterproofing is a water-based self-crosslinking acrylate copolymer emulsion, specially developed as raw material for high-performance waterproof coatings. It adopts emulsion polymerization technology, using water as dispersion medium, free of APEO and heavy metals. After film formation, it forms a continuous, elastic, seamless waterproof membrane with outstanding water resistance, UV resistance, weather resistance and crack-bridging property. It can be directly formulated into exterior wall waterproof coating, roof elastic waterproof coating, transparent waterproof sealer, etc. Widely used in construction waterproof industry.
| Item | Typical Value |
| Appearance | Milky white liquid (becomes transparent/elastic film after drying) |
| Resin Type | Acrylic Emulsion |
| Density | 1.02 – 1.30 g/cm³ |
| Solid Content | 50 – 75% |
| Viscosity (25℃) | 500 – 3000 mPa·s |
| pH Value | 6.5 – 9.0 |
| Tensile Strength | ≥1.0 – 1.8 MPa |
| Elongation at Break | ≥200% (can reach 300–1000%) |
| Tear Strength | ≥10 kgf/cm |
| Adhesion Strength | 0.5 – 1.3 MPa |
| Water Impermeability | 0.3MPa, no water leakage for 30 minutes |
| Low Temp Flexibility | No cracks at -10℃ |
| VOC Content | ≤50 (Environmentally friendly) |
| Surface Dry Time | 2 – 4 hours |
| Fully Cured | 8 – 24 hours |
| Application Temp | 5 – 40℃ |
| Service Temp | -10 – 80℃ |
| UV Resistance | Excellent, no cracks |
| Weather Resistance | Excellent performance and long-term outdoor stability |
| Coverage | 1 – 2 kg/m² |
| Shelf Life | 12-15 months |
Adopt advanced seeded emulsion polymerization technology. Controlled monomer feeding and redox initiation system to synthesize acrylic copolymer with designed Tg. Optimized surfactant package to balance emulsion stability, water resistance and film property. Self-crosslinking functional monomer is introduced into polymer chain. When water evaporates, polymer particles coalesce and crosslink to form dense elastic waterproof membrane. The molecular structure design balances flexibility, tensile strength and outdoor weather resistance.
Acrylic emulsion is a stable dispersion of acrylic polymer particles in water. After coating application, water evaporates gradually. Polymer particles approach, deform and fuse into continuous polymer film. Functional groups on polymer chains react with each other to realize self-crosslinking. The crosslinked polymer film has low water permeability, high elongation and strong adhesion. It can cover micro cracks on substrate and block water penetration, so as to achieve waterproof, anti-seepage and protection effect.