Resin Type: |
Acrylic Emulsion |
Appearance: |
Milky White Liquid (becomes Transparent/elastic Film After Drying) |
Density: |
1.02 – 1.30 G/cm³ |
Water Absorption Of Film: |
≤8% (24h Immersion) |
PH Value: |
6.5 – 9.0 |
VOC Content: |
≤50 (Environmentally Friendly) |
Adhesion Strength: |
0.5 – 1.3 MPa |
Recommended Dosage: |
1.2 – 2.0 Kg/m² (2 Coats) |
Freeze-Thaw Stability: |
5 Cycles, No Coagulation |
Film Breathability: |
Good Water Vapor Permeability |
Resin Type: |
Acrylic Emulsion |
Appearance: |
Milky White Liquid (becomes Transparent/elastic Film After Drying) |
Density: |
1.02 – 1.30 G/cm³ |
Water Absorption Of Film: |
≤8% (24h Immersion) |
PH Value: |
6.5 – 9.0 |
VOC Content: |
≤50 (Environmentally Friendly) |
Adhesion Strength: |
0.5 – 1.3 MPa |
Recommended Dosage: |
1.2 – 2.0 Kg/m² (2 Coats) |
Freeze-Thaw Stability: |
5 Cycles, No Coagulation |
Film Breathability: |
Good Water Vapor Permeability |
Acrylic Emulsion Waterproofing is a waterborne self-crosslinking acrylate copolymer emulsion engineered for high-performance waterproof coatings. Manufactured via emulsion polymerization with water as the dispersion medium, it contains no APEO or heavy metals. Upon film formation, it creates a continuous, flexible and seamless waterproof membrane featuring excellent water resistance, UV stability, weatherability and crack-bridging capacity. It can be directly formulated into exterior wall waterproof coatings, elastic roof waterproof coatings, transparent waterproof sealers and more, serving broad applications in the construction waterproofing sector.
| Item | Typical Value |
| Appearance | Milky white liquid (becomes transparent/elastic film after drying) |
| Resin Type | Acrylic Emulsion |
| Density | 1.02 – 1.30 g/cm³ |
| Solid Content | 50 – 75% |
| Viscosity (25℃) | 500 – 3000 mPa·s |
| pH Value | 6.5 – 9.0 |
| Tensile Strength | ≥1.0 – 1.8 MPa |
| Elongation at Break | ≥200% (can reach 300–1000%) |
| Tear Strength | ≥10 kgf/cm |
| Adhesion Strength | 0.5 – 1.3 MPa |
| Water Impermeability | 0.3MPa, no water leakage for 30 minutes |
| Low Temp Flexibility | No cracks at -10℃ |
| VOC Content | ≤50 (Environmentally friendly) |
| Surface Dry Time | 2 – 4 hours |
| Fully Cured | 8 – 24 hours |
| Application Temp | 5 – 40℃ |
| Service Temp | -10 – 80℃ |
| UV Resistance | Excellent, no cracks |
| Weather Resistance | Excellent performance and long-term outdoor stability |
| Coverage | 1 – 2 kg/m² |
| Shelf Life | 12-15 months |