Product Details
Place of Origin: Shandong China
Brand Name: JIURUNFA
Certification: ISO9001
Model Number: HT-510
Payment & Shipping Terms
Minimum Order Quantity: 1Ton
Price: Negotiable
Packaging Details: 25/50KG woven bag lined with plastic bags, or according to the requirements of customers.
Delivery Time: 7-15 Days
Payment Terms: L/C,T/T,Western Union
Supply Ability: 30000 Ton/Month
Appearance: |
Milky White Liquid (becomes Transparent/elastic Film After Drying) |
Density: |
1.02 – 1.30 G/cm³ |
Viscosity (25℃): |
500 – 3000 MPa·s |
Tensile Strength: |
≥1.0 – 1.8 MPa |
Elongation At Break: |
≥200% (can Reach 300–1000%) |
Freeze-Thaw Stability: |
5 Cycles, No Coagulation |
Adhesion Strength: |
0.5 – 1.3 MPa |
Resin Type: |
Acrylic Emulsion |
Recommended Dosage: |
1.2 – 2.0 Kg/m² (2 Coats) |
Film Breathability: |
Good Water Vapor Permeability |
Appearance: |
Milky White Liquid (becomes Transparent/elastic Film After Drying) |
Density: |
1.02 – 1.30 G/cm³ |
Viscosity (25℃): |
500 – 3000 MPa·s |
Tensile Strength: |
≥1.0 – 1.8 MPa |
Elongation At Break: |
≥200% (can Reach 300–1000%) |
Freeze-Thaw Stability: |
5 Cycles, No Coagulation |
Adhesion Strength: |
0.5 – 1.3 MPa |
Resin Type: |
Acrylic Emulsion |
Recommended Dosage: |
1.2 – 2.0 Kg/m² (2 Coats) |
Film Breathability: |
Good Water Vapor Permeability |
Acrylic Emulsion Waterproofing is a water-based, self-crosslinking acrylate copolymer emulsion designed as a raw material for high-performance waterproof coatings. Made via emulsion polymerization using water as the dispersion medium, it contains no APEO or heavy metals. Once film-formed, it delivers a continuous, elastic, seamless waterproof membrane with excellent water resistance, UV resistance, weather resistance, and crack-bridging ability. It can be directly used to formulate exterior wall waterproof coatings, elastic roof waterproof coatings, transparent waterproof sealers, and more. It is widely applied in the construction waterproofing industry.
| Item | Typical Value |
| Appearance | Milky white liquid (becomes transparent/elastic film after drying) |
| Resin Type | Acrylic Emulsion |
| Density | 1.02 – 1.30 g/cm³ |
| Solid Content | 50 – 75% |
| Viscosity (25℃) | 500 – 3000 mPa·s |
| pH Value | 6.5 – 9.0 |
| Tensile Strength | ≥1.0 – 1.8 MPa |
| Elongation at Break | ≥200% (can reach 300–1000%) |
| Tear Strength | ≥10 kgf/cm |
| Adhesion Strength | 0.5 – 1.3 MPa |
| Water Impermeability | 0.3MPa, no water leakage for 30 minutes |
| Low Temp Flexibility | No cracks at -10℃ |
| VOC Content | ≤50 (Environmentally friendly) |
| Surface Dry Time | 2 – 4 hours |
| Fully Cured | 8 – 24 hours |
| Application Temp | 5 – 40℃ |
| Service Temp | -10 – 80℃ |
| UV Resistance | Excellent, no cracks |
| Weather Resistance | Excellent performance and long-term outdoor stability |
| Coverage | 1 – 2 kg/m² |
| Shelf Life | 12-15 months |
A water-based, eco-friendly coating raw material: non-toxic, low VOC, APEO-free. It films well at room temperature and self-crosslinks on drying. High elasticity and elongation deliver excellent crack bridging, while strong adhesion suits concrete, mortar, stone, metal, and wood. Outstanding UV and weather resistance support long-term outdoor use. It also offers good water, alkali, and mildew resistance, easy compounding with pigments, fillers, and additives, and reliable storage stability with no sedimentation or delamination under normal conditions.
This product serves as a dependable raw material for waterproof coating producers. Supplied as a one-component liquid, it enables easy formulation tuning and provides well-balanced elasticity, water resistance and outdoor durability. It effectively minimizes coating failures such as cracking, peeling and water seepage, while complying with environmental specifications for construction works. Customization of solid content, Tg value and film transparency is available to fit your formulation system. We also guarantee consistent batch-to-batch quality, prompt bulk delivery and favorable cost efficiency for large waterproofing projects.
Ideal as a raw material for exterior wall elastic and roof elastomeric waterproof coatings. Also used in transparent waterproof sealers for stone, tile, and concrete; waterproof and anti-carbonation primers for building facades; balcony, terrace, and window sill waterproof coating bases; anti-rust and waterproof coatings for color steel metal roofs; moisture-proof and anti-seepage coatings for basements under non-permanent immersion; and waterproof repair slurries for micro cracks.
We provide free samples (5–20 kg) for laboratory testing, along with technical formula guidance for coating production. Customization is available for solid content, Tg, transparency, and viscosity. Third-party test report support can be provided upon request, and 24-hour online technical support is available. We also offer OEM & ODM services and on-site technical consultation for formulation issues. Packaging is flexible, with options including 25 kg plastic drums and 1000 kg IBC tanks.
Raw material preparation → Pre-emulsification → Seed polymerization → Semi-continuous monomer feeding → Holding reaction → Cooling, pH adjustment, functional additives → Filtration, inspection, filling, packing → Quality testing & warehouse storage
Store the product at 5–35°C and prevent freezing; frozen emulsion cannot be used. Keep the container sealed after opening and avoid prolonged exposure to air. Avoid contact with strong acids and strong oxidants. Wear gloves and goggles during operation, and if eye contact occurs, rinse with plenty of clean water. Coatings made from this emulsion should not be applied below 5°C or in rainy weather. Do not add excessive water arbitrarily, as this will reduce film strength and waterproof performance. Keep away from children, and dispose of waste liquid according to local environmental regulations. Long-term immersion environments are not recommended unless the formulation is specially adjusted.